LDPE美国陶氏993I、PG7004、PG7008、 低密度聚乙烯树脂不仅仅是通用型聚乙烯树脂，由于它们综合了优异的透明性和挺度、密度特性，它们深受那些期望减少材料用量的加工商的青睐，重新成为一组有价值的产品。由于其加工性比大多数LLDPE树脂方便，以及经过改进的产品性能，使得它们在薄膜应用领域应用非常广泛，它们依然是加工商钟爱的具有成本竞争力的解决方案的选择。这些应用领域涵盖了复杂形状食品包装物、购物袋和带涂层的纸板等。其它典型应用包括内衬材料、透明外包装膜、零售包装袋、重载包装袋、透明收缩膜和零食包装薄膜、复合薄膜、农业用膜、挤塑涂层、帽盖和封闭装置以及很多诸如电缆和玩具等耐用物品的包装等、

DOW™ LDPE 993I

Low Density Polyethylene Resin

陶氏塑料

产品说明：

Low Density Polyethylene (LDPE)

Typical applications include toys, lids, and closures

Good gloss, rigidity, excellent flow

Complies with U.S. FDA 21 CFR 177.152 (c) 2.1

Complies with Canadian HPFB No Objection (With Limitations)

Complies with EU, No 10/2011

Consult the regulations for complete details

DOW Polyethylene 993I Low Density Polyethylene Resin is a medium molecular weight distribution homopolymer designed to offer good gloss and rigidity with excellent flow characteristics. This resin has good processability over a wide range of molding conditions.

物性信息：

基本信息

添加剂	增滑剂 (400 ppm)
机构评级	FDA 21 CFR 177.1520(c) 2.1 HPFB (加拿大) No Objection 2 欧洲 No 10/2011
形式	粒子
加工方法	注射成型

物理性能额定值单位制测试方法

比重	0.923	g/cm³	ASTM D792
熔流率（熔体流动速率） (190°C/2.16 kg)	25	g/10 min	ASTM D1238
抗环境应力开裂 (50°C, **** Igepal, F50)	< 1.00	hr	ASTM D1693

硬度额定值单位制测试方法

肖氏硬度 (邵氏 D)	43		ASTM D2240

机械性能额定值单位制测试方法

抗张强度			ASTM D638
屈服	10.3	MPa	ASTM D638
断裂	11.7	MPa	ASTM D638
伸长率			ASTM D638
屈服	3.0	%	ASTM D638
断裂	40	%	ASTM D638
弯曲模量 - 2% 正割	317	MPa	ASTM D790

冲击性能额定值单位制测试方法

悬壁梁缺口冲击强度 (23°C)	420	J/m	ASTM D256
拉伸冲击强度 1	252	kJ/m²	ASTM D1822

热性能额定值单位制测试方法

载荷下热变形温度 (0.45 MPa, 未退火)	40.0	°C	ASTM D648
脆化温度	-33.9	°C	ASTM D746
维卡软化温度	92.8	°C	ASTM D1525
溶融温度（DSC）	110	°C	内部方法
结晶峰温度 (DSC)	100	°C