美国液氮PA612 IF-1003、IF-1006注塑级 热稳定 高强度
美国液氮PA612 IF-1003、IF-1006、IF-1008、 特点：高冲击强度 ，良好的耐油脂，油，燃料，液压油，水，碱和盐，很好的耐应力龟裂性，即使遭到化学武器袭击时用来掩盖金属零件，低滑动摩擦系数和高抗磨损性，即使在干燥运行时
Nylon 612, Glass Fiber Filler
产品说明：
Forms: Pellets
Processing Method: Injection Molding
Information provided by LNP, a GE Plastics Company.
This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.
物性信息：
| 比重 | 1.32 g/cc | 1.32 g/cc | Method A; ASTM D792 |
| 吸水率 | 0.10 % | 0.10 % | at 24 hrs; ASTM D570 |
| 线性成型收缩率 | 0.0010 - 0.0020 cm/cm | 0.0010 - 0.0020 in/in | ASTM D955 |
| 线性成型收缩率，横向 | 0.0070 - 0.0080 cm/cm | 0.0070 - 0.0080 in/in | ASTM D955 |
| 抗张强度(断裂) | 182 MPa | 26400 psi | ASTM D638 |
| 抗张强度(屈服) | 182 MPa | 26400 psi | ASTM D638 |
| 伸长率 (断裂) | 3.7 % | 3.7 % | ASTM D638 |
| 屈服伸长率 | 3.7 % | 3.7 % | ASTM D638 |
| 拉伸模量 | 9.58 GPa | 1390 ksi | ASTM D638 |
| 弯曲强度 | 290 MPa | 42100 psi | ASTM D790 |
| 弯曲模量 | 9.31 GPa | 1350 ksi | ASTM D790 |
| 悬壁梁缺口冲击强度 | 1.39 J/cm @Thickness 3.18 mm | 2.60 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| 悬壁梁无缺口冲击强度 | 12.4 J/cm @Thickness 3.18 mm | 23.2 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| 悬壁梁缺口冲击强度 | 14.1 kJ/m² | 6.71 ft-lb/in² | ISO 180 |
| 悬壁梁无缺口冲击强度 | 78.3 kJ/m² | 37.3 ft-lb/in² | ISO 180 |
| Falling Dart Impact | 14.0 J | 10.3 ft-lb | ASTM D3763 |
| 冲击试验 | 3.04 J | 2.24 ft-lb | Multi-Axial Instrumented Impact Energy; ISO 6603-2 |
| 线性热膨胀系数 | 40.0 µm/m-°C @Temperature 20.0 °C | 22.2 µin/in-°F @Temperature 68.0 °F | TMA; ASTM E831 |
| 线性热膨胀系数,横向流动 | 72.0 µm/m-°C @Temperature 20.0 °C | 40.0 µin/in-°F @Temperature 68.0 °F | TMA; ASTM E831 |
| 载荷下热变形温度(0.46 MPa) | 214 °C | 417 °F | Unannealed; ASTM D648 |
| 载荷下热变形温度(1.8 MPa) | 198 °C | 388 °F | Unannealed; ASTM D648 |
| 可燃性(UL94) | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in |
| 加工（熔体）温度 | 268 - 274 °C | 514 - 525 °F | |
| 模具温度 | 65.6 - 93.3 °C | 150 - 200 °F | |
| 干燥温度 | 82.2 °C | 180 °F | |
| 干燥时间 | 4 hour | 4 hour | |
| 背压 | 0.172 - 0.345 MPa | 24.9 - 50.0 psi |